Rahimi E, Kalantary S, Babapoor A, Dehghan H, Kazemnejad A, Monazzam Esmaeelpour M. Investigating the Thermal Properties of Hydrated Salt Phase Change Material Nanocomposites in the Prevention of Heat Stress. J Health Saf Work 2025; 15 (2) :271-287
URL: http://jhsw.tums.ac.ir/article-1-7158-en.html
URL: http://jhsw.tums.ac.ir/article-1-7158-en.html
Elnaz Rahimi1 
, Saba Kalantary1 , Aziz Babapoor2 , Habibollah Dehghan3 , Anoshirvan Kazemnejad4 , Mohammadreza Monazzam Esmaeelpour *5
, Saba Kalantary1 , Aziz Babapoor2 , Habibollah Dehghan3 , Anoshirvan Kazemnejad4 , Mohammadreza Monazzam Esmaeelpour *5
1- Department of Occupational Health Engineering, School of Public Health, Tehran University of Medical Sciences, Tehran, Iran
2- Department of Chemical Engineering, University of Mohaghegh Ardabili, P.O. Box 179, Ardabil, Iran
3- Department of Occupational Health Engineering, School of Public Health, Isfahan University of Medical Sciences, Isfahan, Iran
4- Department of Biostatistics, Faculty of Medical Sciences, Tarbiat Modares University, Tehran, Iran
5- Department of Occupational Health Engineering, School of Public Health, Tehran University of Medical Sciences, Tehran, Iran ,smaeel@tums.ac.ir
2- Department of Chemical Engineering, University of Mohaghegh Ardabili, P.O. Box 179, Ardabil, Iran
3- Department of Occupational Health Engineering, School of Public Health, Isfahan University of Medical Sciences, Isfahan, Iran
4- Department of Biostatistics, Faculty of Medical Sciences, Tarbiat Modares University, Tehran, Iran
5- Department of Occupational Health Engineering, School of Public Health, Tehran University of Medical Sciences, Tehran, Iran ,
Abstract: (1659 Views)
Introduction: Wearable thermal management systems and phase change materials (PCMs) have emerged as effective solutions for regulating body temperature and storing thermal energy. This study focuses on synthesizing and thermal optimizing a sodium sulfate decahydrate-based nanocomposite incorporating various nanoparticles to improve its performance for personal thermal regulation applications.
Material and Methods: The composite was prepared using sodium sulfate decahydrate as the base PCM. Potassium chloride (KCl) was added to adjust the melting point, borax (STD) served as a nucleating agent, and sodium polyacrylate (SPA) was included as a thickening agent to suppress phase separation. To evaluate the effect of nanoparticle additives, 0.05 wt.% of aluminum oxide (Al₂O₃), iron oxide (Fe₂O₃), graphene oxide (GO), and titanium dioxide (TiO₂) were separately incorporated into the base formulation. A field emission scanning electron microscope (FESEM) was used to analyze the surface morphology of the resulting nanocomposites. Differential scanning calorimetry (DSC) assessed thermal properties, including phase transition temperatures (melting and freezing points) and latent heat.
Results: Differential scanning calorimetry (DSC) analysis indicated that sample S-5-5 comprising sodium sulfate decahydrate with 3 wt.% KCl, 5 wt.% STD and SPA exhibited a melting temperature of 29.5 °C and a latent heat of 120 J/g. This composition remained stable without phase separation. The incorporation of nanoparticles raised the melting point of the base PCM by 0.6 to 1.72 °C. Aluminum oxide (Al₂O₃) and iron oxide (Fe₂O₃) reduced the latent heat of fusion, whereas GO and TiO₂ increased it.
Conclusion: These findings confirm that the thermal properties of sodium sulfate decahydrate-based PCMs can be tailored by including specific additives and nanoparticles. Hydrated salt nanocomposites demonstrate strong potential as PCMs for wearable body temperature regulation.
Material and Methods: The composite was prepared using sodium sulfate decahydrate as the base PCM. Potassium chloride (KCl) was added to adjust the melting point, borax (STD) served as a nucleating agent, and sodium polyacrylate (SPA) was included as a thickening agent to suppress phase separation. To evaluate the effect of nanoparticle additives, 0.05 wt.% of aluminum oxide (Al₂O₃), iron oxide (Fe₂O₃), graphene oxide (GO), and titanium dioxide (TiO₂) were separately incorporated into the base formulation. A field emission scanning electron microscope (FESEM) was used to analyze the surface morphology of the resulting nanocomposites. Differential scanning calorimetry (DSC) assessed thermal properties, including phase transition temperatures (melting and freezing points) and latent heat.
Results: Differential scanning calorimetry (DSC) analysis indicated that sample S-5-5 comprising sodium sulfate decahydrate with 3 wt.% KCl, 5 wt.% STD and SPA exhibited a melting temperature of 29.5 °C and a latent heat of 120 J/g. This composition remained stable without phase separation. The incorporation of nanoparticles raised the melting point of the base PCM by 0.6 to 1.72 °C. Aluminum oxide (Al₂O₃) and iron oxide (Fe₂O₃) reduced the latent heat of fusion, whereas GO and TiO₂ increased it.
Conclusion: These findings confirm that the thermal properties of sodium sulfate decahydrate-based PCMs can be tailored by including specific additives and nanoparticles. Hydrated salt nanocomposites demonstrate strong potential as PCMs for wearable body temperature regulation.
Keywords: Heat stress, Phase change materials, Nanocomposite, Sodium sulfate decahydrate, Nanoparticles